導電銀漿 | 導電銀膠
Silver Paste

太陽能電池
Solar Cell

Rear silver paste for solar cell (PVMet-305)

太陽能電池|Solar Cell|Rear silver paste for solar cell|PVMet-305

Product Features

  • Low solid content (45-50%)
  • High adhesion (> 3N/mm)
  • High soldering ability
  • Well printability
  • High compatibility with Aluminum paste
  • Lead free

Technical parameters Specifications
Solid content 48±2%
Screen printing 165-250 mesh SS screen
Firing Peak temperature,
750-950℃
Adhesion strength >3N/mm
Adhesion strength after aged
(150℃for 30min)
>2N/mm

Front silver paste for solar cell (PVMet-240)

太陽能電池|Solar Cell|Front silver paste for solar cell|PVMet-240

Product Features

  • High efficiency and low contact resistance
  • Excellent printability and high aspect ratio
  • High adhesion strength
  • Wide IR window

Technical parameters Specifications
Solid content 91±1%
Screen printing 360 mesh SS screen
Firing Peak temperature, 750-950℃
Adhesion strength >2N/mm

Rear silver paste for PERC structure solar Cell (PVMet-360)

太陽能電池|Solar Cell|Rear silver paste for PERC structure solar Cell|PVMet-360

Product Features

  • Less damage to passivation layer
  • High adhesion (> 3N/mm)
  • Excellent aged adhesion (> 2N/mm)
  • High soldering ability
  • Well printability
  • High compatibility with Aluminum paste

Technical parameters Specifications
Solid content 65±5%
Viscosity 52,000 mPa.s @ 25 ℃
#CP52@10rpm/3min
Fineness ≦5um
Screen printing >165-250 mesh SS screen
Firing Peak temperature,
750-950 ℃
Adhesion strength >3N/mm
Adhesion strength after aged
(150℃for 30min)
>2N/mm

觸控面板
Touch Panel

Conductive paste for laser ablation (TPMet-6525)

觸控面板|Touch Panel|Conductive paste for laser ablation|TPMet-6525

Product Features

  • Better yield during laser process for touch panel application
  • Well fine line capability 20/20
  • Excellent dispersion without aggregated particles
  • Good printability
  • Excellent adhesion with ITO/PET, ITO/Glass, CNT/PET, AgNW/PET

Technical parameters Specifications
Solid contents 65-70%
Application method Screen printing
Cure condition 140 ℃ for 40 min

Conductive paste for fine line pattern (TPMet-100)

觸控面板|Touch Panel|Conductive paste for fine line pattern|TPMet-100

Product Features

  • Well fine line capability 50/50 inch for touch panel application
  • Excellent dispersion without aggregated particles
  • Good printability
  • Excellent adhesion with ITO/PET, ITO/Glass, CNT/PET, AgNW/PET

Technical parameters Specifications
Solid contents 70-75%
Application method Screen printing
Cure condition 140 ℃ for 40 min

被動元件
Passive Components

Conductive adhesives for capacitor (CA-103)

被動元件|Passive Components|Conductive adhesives for capacitor|CA-103

Product Features

  • Better performance (extra low ESR) for SMD Al solid electrolytic capacitor
  • Good adhesion with leadframe
  • Excellent process-stability for pad printing

Technical parameters Specifications
Solid contents 80±1%
Application method Pad printing
Cure condition 150 ℃ for 30 min

Conductive electrode for capacitor (CE-070)

被動元件|Passive Components|Conductive electrode for capacitor|CE-070

Product Features

  • Better performance (extra low ESR)
  • Low contact resistance with Carbon layer
  • Excellent process-stability for pad printing

Technical parameters Specifications
Solid contents 60±5%
Application method Pad printing
Cure condition 125 ℃ for 30 min

Conductive electrode for Metal Oxide Varistor (VE-1850)

被動元件|Passive Components|Conductive electrode for Metal Oxide Varistor|VE-1850

Product Features

  • Excellent electrical properties (high surge protection)
  • Good solder-ability
  • Better adhesion strength
  • Excellent printability
  • Wide IR Window

Technical parameters Specifications
Solid contents 82±2%
Application method Screen printing
Cure condition 500-600 ℃ for 30 min
Pencil harden >H